Process for breaking petroleum emulsions



Patented Feb. 26, 1951 ATES PA atlas-s T OFFICE PROCESSES-FOR. BREAKING PETROLEUM EMUILSIONS No Drawing. Applic' on December 13, .1948,

will

Serial No. 65,086

llClaims. (Cl. 252341) This invention relates to processes or -procedures particularly adapted for preventing, breaking or=resolving emulsions of the' water-inoil a type; and particularly petroleum" emulsions. This invention is a-co-ntinuation-in-part of our co-pending' application Serial No.- 726,298,- filed February 3, 194? (nowabandoned). See our copending applications Serial No. 8,731, filed February 16, 1948 (now abandoned), and also Serial No. 82,704, filed March 21, 19%9 (now Patent No.-

ing said new chemical products"or-compounds which are of outstanding value in demulsific'ation. Seeour co-pending; application Serial No."

65,087, filed December 13, 19431 Our invention provides an' economicaland' rapid process for resolving petroleumemulsions of the water-in-oi1 type, that are'common1y're'-' ferredtoavcut oil, roily oil, emulsified oil, etc, and ch comprise fine droplets of naturally-cc g waters 'onbrines dispersed in a mcreor less permanent state throughout -the-oil which constitutes the-ccntinuous phase of the emulsion.

It also provides an economical and rapid process-for separating emulsions which have been prepared 1 under controlled conditions from mineral 5011,15 waters'o-r .brinesx Controlled emulsification and en .uent demulsificatlen, under the conremoving impundes; particularly inorganic salts, from pipeline oil.

Demulsification, as, contemplated in the presentapplication, includes the-preventive step of commingling the demulsifier with theaqueouscomponent which wou'd or might subsequently become either phase. of the emulsion inthecabsence of such precautionary measure. Similarly, such demu-lsifier may be 'mixedwithz the hydro carbon component.

as. crude oil and'relativey soft oped, are of significant: value in- Briefly stated, the present process is concerned with the breaking or resolving of petroleum emulsions by means of quaternary ammonium compounds obtained'from certain esters which are, in turn, derivatives of specific synthetic products. These products are, in turn, the oxyalkylated derivatives of certain resins hereinafter specified.

Thus, the present process is concerned with breaking petroleum emulsions of the water-in-oi1 type, characterized by subjecting the emulsion to specific hydrophile quaternary ammonium compounds, hereinafter described. Said hydrophile quaternary ammonium compounds are obtained by reaction between a hydroxylatedglyoxalidine of the formula:

in which RC is the residue of the radical RCO, which, in turn, is the acyl radical of a detergentforming monoc-arboxy acid having at least 8 and not more than 22 carbon atoms, and R10 is an alkylene oxide radical having not over 4 carbon atoms and selected from the class consisting of ethylene oxide radicals, propylene oxide radicals, butylene oxide radicals, glycide radicals, and methylglycide radicals; and n is a numeral Varying from 1 to 3; and the ester of an alphahalogen monocarboxyiic'acid having not over 6 carbonatoms and hydrophile hydroxylated synthetic products; said hydrophile synthetic products being oxyalkylation' products of (A) an alpha-beta alkylene oxide having not more than carbon atoms and selected from the class consisting of ethylene oxide, propylene oxide, butylene oxide, glycide, and methylglycide; and (B) an oxyalkylation-susceptible,- fusible, organic solvent-soluble, water-insoluble, phenol-aldehyde resin; said resin being derived by reaction between a difunctional monohydric phenol and an aldehyde having not over 8 carbon atoms and reactive towards said phenol; said resin being formed in the substantial absence of trifunctional p enols; said phenol being of the formula:

in which R is a hydrocarbon radical having at least 4 and not more than 12 carbon atoms and substituted in the 2,4,6 position; said oxyalkyl ated resin being characterized by the introduction into the resin molecule of a plurality of divalent radicals having the formula (R)n, in which R1 is a member selected from the class consisting of ethylene radicals, propylene radicals, butylene radicals, hydroxypropylene radicals, and hydroxybutylene radicas, and n is a numeral varying from 1 to with the proviso that at least 2 moles of alkylene oxide be introduced for each phenolic nucleus; and with the final proviso that the hydrophile properties of the ultimate quaternary ammonium compound as well as the oxyalkylated resin in an equal weight of xylene are sufiicient to produce an emulsion when said xylene soution is shaken vigorously with one to three volumes of water.

For convenience, what is said hereinafter may be divided into five parts. Part 1 will be concerned with the production of the resin from a difunctional phenol and an aldehyde; Part 2 will be concerned with the oxyalkylation of the resin so as to convert it into a hydrophile hydroxylated derivative; Part 3 will be concerned with the conversion of the immediately aforementioned derivative into a total or partial ester by reaction with chloroacetic acid, or the like; Part 4 will be concerned with the reaction between such esters containing a labile halogen and the hydro-xylated glyoxalidine, as described; and Part 5 will be concerned with the use of such quaternary ammonium compounds as demulsifiers, as hereinafter described.

PART 1 As to the preparation of the phenol-aldehyde resins reference is made to our co-pending applications, Serial Nos. 8,730 and 8,731, both filed February 16, 1948 (both now abandoned). In such co-pending applications we described a fusible, organic solvent-soluble, Water-insoluble resin polymer of the formula OH on OH H I n -c-- o H H R R n R In such idealized representation n" is a numeral varying from 1 to 13 or even more, provided that the resin is fusible and organic solvent-soluble. R is a hydrocarbon radical having at least 4 and not over 8 carbon atoms. In the instant application R may have as many as 12 carbon atoms, as in the case of a resin obtained from a dodecylphenol. In the instant invention it may be first suitable to describe the alkylene oxides employed as reactants, then the aldehydes, and finally the phenols, for the reason that the latter require a more elaborate description.

The alkylene oxides which may be used are the alpha-beta oxides having not more than 4 carbon atoms, to wit, ethylene oxide, alpha-beta propylene oxide, alpha-beta butylene oxide, glycide, and methylglycide.

Any aldehyde capable of forming a methylol or a substituted methylol group and having not more than 8 carbon atoms is satisfactory, so long as it does not possess some other functional group or structure which will conflict with the resinifioation reaction or with the subsequent oxyalkylation of the resin, but the use of formaldehyde, in its cheapest form of an aqueous solution, for the production of the resins is particularly advanta-' geous. 'Solid polymers of formaldehyde are more expensive and higher aldehydes are both less reactive, and are more expensive. Furthermore, the higher aldehydes may undergo other reactions which are not desirable, thus introducing difficulties into the resinification step. Thus acetaldehyde, for example, may undergo an aldol condensation, and it and most of the higher aldehydes enter into self-resinification when treated with strong acids or alkalies. On the other hand, higher aldehydes frequently beneficially affect the solubility and fusibility of a resin. This is illustrated, for example, by the diiferent characteristics of the resin prepared from para-tertiary amylphenol and formaldehyde on one hand, and a comparable product prepared from the same phenolic reactant and heptaldehyde on the other hand. The former, as shown in certain subsequent examples, is a hard, brittle, solid, whereas the latter is soft and tacky, and obviously easier to handle in the subsequent oxyalkylation procedure.

Cyclic aldehydes may be employed, particularly benzaldehyde. The employment of furfural requires careful control for the reason that in addition to its aldehydic function, furfural can form vinyl condensations by virtue of its unsaturated structure. The production of resins from furfural for use in preparing reactants for the present process is most conveniently conducted with weak alkaline catalysts and often with alkali metal carbonates. Useful aldehydes, in addition to formaldehyde, are acetaldehyde, propiom'c aldehyde, butyraldehyde, Z-ethylhexanal, ethylbutyraldehyde, heptaldehyde, and benzaldehyde, furfural and glyoxal. It would appear that the use of glyoxal should be avoided due to the fact that it is tetrafunctional. However, our experience has been that, in resin manufacture and particularly as described herein, apparently only one of the aldehydic functions enters into the resinification reaction. The inability of the other aldehydic function to enter into the reaction is presumably due to steric hindrance. Needless to say, one can use a mixture of two or more aldehydes although usually this has no advantage.

Resins of the kind which are used as intermediates in this invention are obtained with the use of acid catalysts or alkaline catalysts, or without the use of any catalyst at all. Among the useful alkaline catalysts are ammonia, amines, and quaternary ammonium bases. It is generally accepted that when ammonia and amines are employed as catalysts they enter into the condensation reaction and, in fact, may operate by initial combination with the aldehydic reactant. The compound hexamethylenetetramine illustrates such a combination; In light of these various reactions it becomes difficult to present any formula which would depict the structure of the various resins prior to oxyalkylation. More will be said subsequently as to the difference between the use of an alkaline catalyst and an acid catalyst; even in the use of an alkaline catalyst there considerable evidence to indicate that the products are not identical where different basic materials are employed. The basic materials employed inolude'not only those previously enumerated but also the hydroxides of the alkali metals, hydroxides of the alkaline earth metals, salts of strong bases and weak acids such as sodium acetate, etc.

Suitable jnhenolic reactants include ,the followfins: Para rtiarybutylphenol; para-secondarybutylphenol; para-tertiary-amylphenol; paraecondaryea lphenol; .pa t r i ry-hexy p .nol; zpara-isooctylphenol; ortho-phenylphenol;

ortho-benzylphenol; parabenzylphenol; and para-cyclohexylphenol, and .the corresponding ortho-para substituted metacresols and 3,5-xylenols. Similarly, one may use paraor ortho-nonylphenol or .a mixture, paraor ortho-dccylphenol-or a mixture, menthylphenol, or paraor ortho-dodecylphenol.

For convenience, the phenol has previously been referred to as monocyclic in order to differentiate from fused nucleus polycyclic phenols, such as substituted naphthols. Specifically, monocyclic islimited to the nucleus in which the hydroxyl radical is attached. Broadly speaking, where a substituent is cyclic, particularly aryl, obviously in the usual sense such phenol is actually polycyclic although the phenolic hydroxyl is not attached to a fused polycyclic nucleus. Stated another way, phenols in which the hy- -,droxyl .group is directly attached to a condensed or fused polycyclic structure, are excluded. This matter, however, is clarified by the following consideration. The phenols herein contemplated for reaction may be indicated by the following formula:

in which R ,is selected from :the class Consisting cfhydrogen atoms and hydrocarbon radicals having at least 4 carbon atoms and not more than 12 carbon atoms, with the proviso that one 0.8- currence of R is the hydrocarbon substituent and the other two occurrences are hydrogen atoms, and with the further provision that one or :leoth-of the 3 and 5 positions may be methyl substituted.

The above formula possibly can be restated more conveniently in the following manner, to wit, that the phenol employed is of the following formula, with the proviso that Ris a hydrocarbon substituent located in the 2,4,6 position, again with the provision as to 3 or 3,5 methyl substitution. This is conventional nomenclature, numbering the various positions in the usual clockwise manner, beginning with the hydroxyl position as one:

6 :trade and :oil solubility is .of prime importance. .For'this reason, the .common reactants employed :arebutylated phenols, 'amylated phenols, phenylphenols, etc. The methods employed in manufacturing such resins are similar to those employed in the manufacture of ordinary phenolformaldehyde resins, in that either an acid or alkaline catalyst is usually employed. The procedure usually differs from that employed in the manufacture of ordinary phenol-aldehyde resins in that phenol, being Water-soluble, reacts readily with an aqueous aldehyde solution without further difliculty, while when a water-insoluble phenol is employed some modification is usually adopted to increase the interfacial surface and thus cause reaction to take place. A common solvent is sometimes employed. Another procedure employs rather severe agitation to create a large interfacial area. Once the reaction starts .to a moderate degree, it is possible that both reactants are somewhat soluble in the partially reacted mass and assist in hastening the reaction. We have found it desirable to employ a small proportion of .an organic sulfo-acid as a catalyst, either alone oralong with a mineral acid like sulfuric or hydrochloric acid. For example, alkylated aromatic sulfonic acids are effectively employed. Since commercial forms of such acids are commonly their alkali salts, it is sometimes convenient to use a small quantity of such alkali salt plus a small quantity of strong mineral acid, as shown in the examples'below. If desired, such organic sulfo-acids may be prepared in situ in the phenol employed, b reacting concentrated sulfuric .acid with a small proportion of the phenol. In such cases where xylene is used as a solvent and concentrated sulfuric acid is employed, some sulfonation of the xylene probably occurs to produce the sulfa-acid. Addition of a solvent .such as xylene is advantageous as hereinafter described in detail. Another variation of procedure is to employ such organic sulfo-acids, in the form of their salts, in connection with an alkali-catalyzed resinification procedure. Detailed examples are included subsequently.

.Another advantage in the manufacture of the thermoplastic or fusible type of resin by the acid catalytic procedure is that, since a difunctional phenol is employed, an excess of an aldehyde, for instance formaldehyde, may be employed without too marked a change in conditions of reaction and ultimate product. There is usually little, if any, advantage, however, in using an excess over and above the stoichiometric proportions for the reason that such excess may be lost and wasted. For all practical purposes the molar ratio of formaldehyde to phenol may be limited to 6.9 to 1.2, with 1.05 as the preferred ratio, or sufficient, at least theoretically, to convert the remaining reactive hydrogen atom of each terminal phenolic nucleus. Sometimes when higher aldehydes are used an excess of aldehyde reactant can be distilled off and thus recovered from the reaction mass. This same procedure be used with formaldehyde and excess reactant re covered.

When an alkaline catalyst is used the amount of aldehyde, particularly formaldehyde, may be increased over the simple stcichiometric ratio of one-to-one or thereabouts. With the use of alkaline catalyst it has been recognized that considerably increased amounts of formaldehyde may be used, as much as two moles of formaldehyde, for example, per mole of phenol, or even more, with the result that only .a small part of such aldehyde remains uncombined or is subsequently liberated during resinification. Structures which have been advanced to explain such increased use of aldehydes are the following:

OH OH Such structures may lead to the production ofcyclic polymers instead of linear polymers. For this reason, it has been previously pointed out that, although linear polymers have by far the most important significance, the present invention does not exclude resins of such cyclic structures.

Sometimes conventional resinification procedure is employed using either acid or alkaline catalysts to produce low-stage resins. Such resins may be employed as such, or may be altered or converted into high-stage resins, or in any event, into resins of higher molecular weight, by heating along with the employment of vacuum so as to split off water or formaldehyde, or both. Generally speaking, temperatures employed, particularly with vacuum, may be in the neighborhood of 1T5 to 256 0., or thereabouts.

It may be well to point out, however, that the amount of formaldehyde used may and does usually afiect the length of the resin chain. Increasing the amount of the aldehyde, such as formaldehyde, usually increases the size or molecular weight of the polymer.

In the hereto appended claims there is specifled, among other things, the resin polymer con-- taining at least 3 phenolic nuclei. Such minimum molecular size is most conveniently determined as a rule by cryoscopic method using benzene, or some other suitable solvent, for instance, one of those mentioned elsewhere herein as a solvent for such resins. As a matter of fact, using the procedures herein described or any conventional resinification procedure will yield produ=: usually having definitely in excess of 3 nuclei. In other words, a resin having an average of 4, 5 or 5 nuclei per unit is apt to be formed as a minimum in resinification, except under certain special conditions where dimerization occur.

However, if resins are prepared at substantially higher temperatures, substituting cymene, tetralin, etc, or some other suitable solvent which boils or refiuxes at a higher temperature, instead of xy..ene, in subsequent examples, and if one doubles or triples the amount of catalyst, doubles- Sometimes the expression 1 The molecular weight determinations, of course, require that the product be completely soluble in the particular solvent selected as, for instance, benzene. The molecular weight determination of such solution may involve either the freezing point as in the cryoscopic method, or, less conveniently perhaps, the boiling point in an ebullioscopic method. The advantage of the ebullioscopic method is that, in comparison with the cryoscopic method, it is more apt to insure complete solubility. One such common method to employ is that or Menzies and Wright (see J. Am. Chem. Soc. 43, 2309 and 2314 (1921)). Any suitablemethod for determining molecular weights will serve, although almost any procedure adopt-'- ed has inherent limitations. A good method for determining the molecular weights of resins,

' especially solvent-soluble resins, is the cryoscopic such as xylene, as hereinafter illustrated in detail. However, we have obtain-ed products from resins obtained by use of an alkaline catalyst which were just as satisfactory as those obtained employing acid catalysts. Sometimes a combination of both types of catalysts is used in different stages of resinification. Resins so obtained are also perfectly satisfactory.

In numerous instances the higher molecular weight resins, i. e., those referred to as highstage resins, are conveniently obtained by subjecting lower molecular weight resins to vacuum distillation and heating. Although such procedure sometimes removes only a modest amount or even perhaps no low polymer, yet it is almost certain to produce further polymerization. For instance, acid catalyzed resins obtained in the usual manner and having a molecular weight indicating the presence of approximately 4 phenolic units or thereabouts may be subjected to such treatment, with the result that one obtains a resin having approximately double this molecular weight. The usual procedure is to use a secondary step, heating the resin in the presence or absence of an inert gas, including steam, or by use of vacuum.

We have found that under the usual conditions of resinification employing phenols of the kind here described, there is little or no tendency to form binuclear compounds, i. e., dimers, resulting from the combination, for example, of 2 moles of a phenol and one mole of formaldehyde, particularly where the Substituent has 4 or 5 carbon atoms. Where the number of carbon atoms in a substituent approximates the upper limit specified herein, there may be some tendency to dimerization. The usual procedure to obtain a dimer involves an enormously large excess of the ,phenol, for instance, 8 to 10 moles per moleof aldehyde.

Substituted dihydroxydiphenylmethanes obtained from substituted phenols are not resins as that term is used herein.

Although any conventional procedure ordinarily employed may be used in the manufacture of the herein contemplated resins or, for that matter, such resins may be purchased in the open market, we have found it particularly desirable to use the procedures described elsewhere herein.

amaqoa and employing a combination of an organic sulfoacid and a mineral acid as a catalyst, and xylene as a solvent. By way of illustration, certain subsequent examples are included, but it is to be understood the herein described invention is not concerned with the resins per se or with any particular method of manufacture but is concerned with the use of reactants obtained by the subsequent oxyalkylation thereof. The phenolaldehyde resins may be prepared in any suitable manner.

Oxyalkylation, particularly oxyethylation which is the preferred reaction, depends on contact between a non-gaseous phase and a gaseous phase. It can, for example, be carried out by melting the termoplastic resin and subjecting it to treatment with ethylene oxideor the like, or by treating a suitable solution or suspension. Since the melting points of the resins are often higher than desired in the initial stage of oxyethylation, we have found it advantageous to use a solutionor suspension of thermoplastic resin in an inert solvent such as xylene. Under such circumstances, the resin obtained in the usual manner is dissolved by heating in xylene undera. reflux condenser or in any other suitable manner. Since xylene or an equivalent inert solvent is present or may be present during oxyalkylation, it is obvious there is no objection to having a solvent present during the resinifying stage if, in addition to being inert towards the resin, it is also inert towards the reactants and also inert towards water. Numerous solvents, particularly of aromatic or cyclic nature, are suitably adapted for such use. Examples of such solvents are xylene, cymene, ethyl benzene, propyl benzene, mesityl-ene, decalin (decahydronaphthalene) tetralin (tetrahydronaphthalene), ethylene glycol diethylether, diethylene glycol diethylether, and tetraethylene glycol dimethylether, or mixtures of one or more. Solvents such as dichloroethylether, or dichloropropylether may be employed either alone or in mixture but have the objection that the chlorineatom in the compound may slowly combine with the alkaline catalyst em ployed in oxyethylation. Suitable solvents may be selected from this group for molecular weight determinations.

The use of such solvents is a convenient expedient in the manufacture of the thermoplastic,

resins, particularly since the solvent gives amore liquid reaction mass and thus prevents overheating, and also because the solvent can be,

employed in connection with a. reflux condenser and a water trap to assist in the removal of water of reaction and also water present aspart of the formaldehyde reactant when an aqueous solution of formaldehyde is used. Such aqueous solution, of course, with the ordinary product. of

stances it is most desirable to permit part of the solvent, particularly when it is inexpensive, e. g., xylene, to remain behind in a predetermined amount so as to have a resin which can be handled more conveniently in the oxyalkylation stage. If a more expensive solvent, such as decalin, is employed, xylene or other inexpensive solvent may be added after the removal of decalin, if desired.

In preparing resins from difunctional phenols it is common to. employ reactants of technical grade. The substituted phenols herein contemplated are usually derived from hydroxybenzene. As a rule, such substituted phenols are comparatively free from unsubstituted phenol. We have generally found that the amount present is considerably less than 1% and not infrequently in the neighborhood of of 1%, or even less. The amount of the usual trifunctional phenol, such ashydroxybenzene or metacresol, which can be tolerated is determined by the fact that actual cross-linking, if it takes place even infrequently, must not be sufficient to cause insolubility at the completion of the resinification stage or the lack of hydrophile properties; at the completion of the oxyalkylation stage.

The exclusion of; such trifunctional phenols as hydroxybenzene or metacresol is not based on the fact that the mere random or occasional inclusion of an unsubstituted phenyl nucleus in the resin molecule or inone of several molecules, for example, markedly alters the characteristics of the oxyalkylated derivative. The presence of a phenyl radical having a reactive hydrogen atom available or having a hydroxymethylol or a substituted hydroxymethylol group present is a potential source of cross-linking either during resinification or oxyalky-lation. Cross-linking leads either to insoluble resins or to non-hydrophilic products resulting from the oxyalkylation procedure. Withthis rationale understood, it is obvious that trifunctional phenols are tolerable only in a minor proportion and should not be present to the extent that insolubility is produced in the resins, or thatthe product resulting from oxyalkylation is gelatinous, rubbery, or at least not hydrophile. As to the rationale of resinification, note particularly what is said hereafter in differentiating between resoles, Novolaks, and resins obtained solely from difunctional phenols.

Previousreference has been made to the fact that fusible organic solvent-soluble resins are usually linear but may be cyclic. Such more complicated structure may be formed, particularly if a resin prepared in the usual manner is converted into a higher stage resin by heat treatment in vacuum as previously mentioned. Thisagain is a. reason for avoiding any opportunity for cross-linking due to the presence of any appreciable amount of trifunctional phenol. In other words, the presence: of such reactant may cause cross-linking. in a conventional resinificationprocedure. or in the oxyalkylation procedure, or in the heat and vacuum treatment if it is employed as part of resin manufacture.

Our routine procedure in examining a phenol for suitability for preparing intermediates to be used inpracticing the invention is to prepare a resin employing formaldehyde in excess (1.2'molesof formaldehyde. per mole of phenol) and using an acid catalyst in the manner described in Example 1a of our Patent 2,499,370 granted March 7, 1950. If the resin so obtained is solvent-soluble-in any one of the aromatic or other solvents previous y referred to, it is then subjected to oxyethylation. During oxyethylation a temperature is employed of approximately to C with addition of at least 2 and advantageously up to 5 moles of ethylene oxide per phenolic hydroxyl. The oxyethylation is advantageously conducted so as to require from a ii few minutes up to to hours. If the product so obtained is solvent-soluble and self-dispersing or emulsifiable, or has emulsifying properties, the phenol is perfectly satisfactory from the standpoint of tr-ifunctional phenol content. The solvent may be removed prior to the dispersibility or emulsifiability test. When a product becomes rubbery during oxyalkylation'due to the presence of a small amount of trireactive phenol, as previously mentioned, or for some other reason, it may become extremely insoluble, and no longer qualifies as being hydrophile as herein specified. Increasing the size of the aldehydic nucleus, for instance using heptaldehyde instead of formaldehyde, increases tolerance for trifunctional phenol.

The presence of a trifunctional or tetrafunctional phenol (such as resorcinol or bisphenol A) is apt to produce detectable cross-linking and insolubilization but will not necessarily do so, especially if the proportion is small. Resinification involving difunctional phenols only may also produce insolubilization, although this seems to be an anomaly or a contradiction of what is sometimes said in regard to resinification reactions involving difunctional phenols only. This is presumably due to cross-linking. This appears to be contradictory to what one might expect in light of the theory of functionality in resinification. It is true that under ordinary circumstances, or rather under the circumstances of conventional resin manufacture, the procedures employing difunctional phenols are very apt to, and almost invariably do, yield solvent-soluble, fusible resins. However, when conventional procedures are employed in connection with resins for varnish manufacture or the like, there is involved the matter of color, solubility in oil, etc. When resins of the same type are manufactured for the herein contemplated purpose, i. e., as a raw material to be subjected to oxyalkylation, such criteria of selection are no longer pertinent. Stated another way, one may use more drastic conditions of resinification than those ordinary employed to produce resins for the present purposes. Such more drastic conditions of resinification may include increased amounts of cata-' lyst, higher temperatures, longer time or" reacion, subsequent reaction involving heat alone or in combination with vacuum, etc. Therefore, one is not only concerned with the resinification reactions which yield the bulk of ordinary resins from difunctional phenols but also and particularly with the minor reactions of ordinary resin manufacture which are of importance in the present invention for the'reason that they occur under more drastic conditions of resinification which may be employed advantageously at times, and they may lead to' cross-linking.

In this connection it may be well to point out that part of these reactions are now understood or explainable to a greater or lesser degree in light of a most recent investigation. Reference is made to the researches of Zinke and his 00- workers, Hultzsch and his associates, and to von Eulen and his co-workers; and others. As to a bibliography of such investigations, see Carswell, Phenoplasts, chapter 2. These investigators limited much of their work to reactions involving phenols having two or less reactive hydrogen atoms. Much of what appears in these most recent and most up-to-date investigations is pertinent to the present invention insofar that much of it is referring to resinification involving difunctional phenols.

' stage.

V For the moment, it may be simpler to consider a most typical type of fusible resin and forget for the time that such resin, at least under certain circumstances, is susceptible to further complications. Subsequently in the text it will be pointed out that cross-linking or reaction with excess formaldehyde may take place even with one of such .most typical type resins.

This point is made for the reason that insolubles I must be avoided in order to obtain the products herein contemplated for use as reactants.

The typical type of fusible resin obtained from a para-blocked or ortho-blocked phenol is clearly differentiated from the Novolak type or resole type of resin. Unlike the resole type, such typical type para-blocked or ortho-blocked phenol resin may be heated indefinitely without passing into an infusible stage, and in this respect is similar to a Novolak. Unlike the Novolak type the addition of a further reactant, for instance, more aldehyde, does not ordinarily alter fusibility of the difunctional phenol-aldehyde type resin; but such addition to a Novolak causes cross-linking by virtue of the available third functional position.

What has been said immediately preceding is subject to modification in this respect: it is well known, for example, that difunctional phenols, for instance, paratertiaryamylphenol, and an aldehyde, particularly formaldehyde, may yield heat-hardenable resins, at least under certain conditions, as for example the use of two moles; of formaldehyde to one of phenol, along with an alkaline catalyst. This peculiar hardening orcuring or cross-linking of resins obtained from; difunctional phenols has been recognized by; various authorities.

The intermediates herein used must be hydro-. phile or sub-Surface-active or surface-active as; hereinafter described, and this precludes the formation of insolubles during resin manufactureor the subsequent stage of resin manufacture, where heat alone, or heat and vacuum, are em.. ployed, or in the oxyalkylation procedure. In its;

' simplest presentation the rationale of resinifi-.

cation involving formaldehyde, for example, and a difunctional phenol would not be expected to. form cross-links. However, cross-linking some-. times occurs and it may reach the objectionable: However, provided that the preparation; of resins simply takes into cognizance the present knowledge of the subject, and employing preliminary, exploratory routine examinations as. herein indicated, there is not the slightest difficulty in preparing a very large number of resins: of various types and from various reactants, and by means of different catalysts by different procedures, all of which are eminently suitable for the herein described purpose.

Now returning to the thought that cross-linking can take place, even when difunctional phe nols are used exclusively, attention is directed to the following: Somewhere during the course of resin manufacture there may be a potential cross-linking combination formed but actual cross-linking may not take place until the subsequent stage is reached, i. e., heat and vacuum stage, or oxyalkylation stage. This Situation may be related or explained in terms of a theory of flaws, or Lockerstellen, which is employed in explaining flaw-forming groups due to the fact that a CHzOl-I radical and H atom may not lie in the same plane in the manufacture of ordinary phenol-aldehyde resins.

Secondly, the formation or absence of formaangers tion of insolubles may be related to the aldehyde used and the ratio of aldehyde, particularly formaldehyde, insofar that a slight variation may, under circumstances not understandable, produce insolubilization. The formation of the insoluble resin is apparently very sensitive to the quantity of formaldehyde employed and a slight increase in the proportion of formaldee hyde may lead to the formation of insoluble gel lumps. Ihe cause of insoluble resin formation is not clear, and nothing is known as to the structure of these resins.

All that has been said previously herein as regards resiniiication has avoided the specific reference to activity of a methylene hydrogen atom. Actually there is a possibility that under some drastic conditions cross-linking may take place through formaldehyde addition to the methylene bridge, or some other reaction involving a methylene hydrogen atom.

Finally, there is some evidence that, although the meta positions are not ordinarily reactive, possible at times methylcl groups or the like are formed at the meta positions; and if this were the case it may be a suitable explanation of abnormal cross-linking.

Reactivity of a resin towards excess aldehyde, for instance formaldehyde, is not to be taken as a criterion of rejection for use as a reactant. In other words, a phenol-aldehyde resin which is thermoplastic and solvent-soluble, particularly if Xylene-soluble, is perfectly satisfactory even though retreatment with more aldehyde may change its characteristics markedl in regard to both fusibility and solubility. Way, as far as resins obtained from difunctional phenols are concerned, they may be either formaldehyde-resists nt or not formaldehyde-resistant.

Referring again to the resins herein contemplated as reactants, it is to be noted that they are thermoplastic phenol-aldehyde resins derive-cl from difunctional phenols and are clearly distinguished from Novolaks or resoles. When these.

resins are produced from diiunctional phenols and some of the higher aliphatic aldehydes, such as acetaldohyde, the resultant is often a comparatively soft or pitchlike resin at ordinar temperature. Such resins become comparatively fluid at 110 to 165 C. as a rule and thus can be readily oxyalkylated, preferably oxyethylated, without the use of a solvent.

Reference has been made to the use of the word fusible. Ordinarily a thermoplastic resin is identified as one which can be heated repeatedly and still not lose its thermoplasticity. It is recognized, however, that one may have a resin which is initially thermoplastic but onrepeated heating may become insoluble in an organic solvent, or at least no longer thermoplastic, due to the fact that certain changes take place very slowly. As far as the present invention is concerned, it is obvious that a resin to be suitable need only be sufficiently fusible to permit processing to produce our oxyalkylated products and not yield insolubles or cause insolubilization or gel formation, or rubberiness, as previously described. Thus resins which are, strictly speaking, fusible but not necessarily thermoplastic in the most rigid sense that such terminology would be applied to the mechanical properties of a resin, are useful intermediates. The bulk of all fusible resins of the kind herein described are thermoplastic.

The fusible or thermoplastic resins, or solventsoluble resins, herein employed as reactants, are

Stated another wat1"-insoluble, or have no appreciable hydro phile properties. The hydrophile property is introduced by oxyalkylation. In the hereto appended claims and elsewhere the expression Water-insoluble is used to point out this characteristic of the resins used.

In the manufacture of compounds herein employed, particularly for demulsification, it is obvious that the resins can be obtained by one of a number of procedures. In the first place, suitable resins are marketed by a number of companies and can be purchased in the open market; in the second place, there are a wealth of examples of suitable resins described in theliterature. The

third procedure is to follow the directions of the present application.

The polyhydric reactants, i. e., the oxyalkylation-susceptible, water-insoluble, organic solventsoluble, fusible, phenol-aldehyde resins derived from diiunctional phenols, used as intermediates to produce the products used in accordance with the invention, are exemplified by Examples Nos. 1a through 103a of our Patent 2,499,376, granted March 7, 1950, and reference is made to that patent for examples of the oxyalkylated resins used as intermediates.

Previous reference has been made to the use of a single phenol as herein specified, or a single reactive aldehyde, or a single oxyalkylating agent. Obviously, ixtures of reactants may be employed, as for example a mixture of para-butylphenol and para-amylphenol, or a mixture of para-butylphenol and para-hexylphenol, or parabutylphenol and para-phenylphenol. It is extremely difiicult to depict the structure of a resin derived from a single phenol. When mixtures of phenols are used, even in equimolar proportions, the structure of the resin is even more indeterminable. In other words, a mixture involving para-butylphenol and para-amylphenol might have an alternation of the two nuclei or one might have a series of butylated nuclei and then a series of amylated nuclei. If a mixture of aldehydes is employed, for instance, acetaldehyde and butyraldehyde, or acetaldehyde and formaldehyde, or benzaldehyde and acetaldehyde, the final structure of the resin bocomes even more complicated and possibly depends on the relative reactivity of the aldehydes. For that matter, one might be producing simultaneously two different resins, in what would actually be a mechanical mixture, although such mixture might exhibit some unique properties as compared with a mixture of the same two resins prepared separately. Similarly, as has been suggested, one might use a combination of oxyalkylating agents; for instance, one might partially oxyalkylate with ethylene oxide and then finish off with propylene oxide. It is understood that the oxyalkylated derivatives of such resins, derived from such plurality of reactants, instead of being limited to a single reactant from each of the three classes, is contemplated and here included for the reason that they are obvious variants.

PART 2 Having obtained a suitable resin oi the kind described, such resin is subjected to treatment with a low molal reactive alpha-beta olefin oxide so as to render the product distinctly hydrophile in nature as indicated by the fact that it becomes self-emulsifiable or miscible or soluble in water, or self-dispersible, or has emulsifying properties.

15 The olefin oxides employed are characterized by the fact that they contain not over 4 carbon atoms and are selected from the class consisting V of ethylene oxide, propylene oxide, butylene oxide,

glycide, and methylglycide. Glycide maybe, of course, considered as a hydroxy propylene oxide and methyl glycide as a hydroxy butylene oxide. In any event, however, all such reactants contain the reactive ethylene oxide ring and may be best considered as derivatives of or substituted ethylene oxides. The solubilizing effect of the oxide is directly proportional to the percentage of oxygen present, or specifically, to the oxygen-carbon ratio. a W i In ethylene oxide, the oxygen-carbon ratio is 1:2. In glycide, it is 2:3; and in methyl glycide, 1 :2. In such compounds, the ratio is very favorable to the production of hydrophile or surfaceactive properties. However, the ratio, in propylene oxide, is 1:3, and in butylene oxide, 1:4. Obviously, such latter two reactants are satisfactorily employed only where the resin composition is such as to make incorporation of the desired property practical. Inother cases, they may produce marginally satisfactory derivatives, or even unsatisfactory derivatives. They are usable in conjunction with the three more favorable alkylene oxides in all cases. For instance, after one or several propylene oxide or butylene oxide molecules have been attached to the resin molecule, o-xyalkylation may be satisfactorily con-- tinued using the more favorable members of the class, to produce the desired hydrophile product. Used alone, these two reagents may in some cases fail to produce sufficiently hydrophile derivatives because of their relatively low oxygen-carbon ratios.

Thus, ethylene oxide is much more effective than ethylen oxide, and butylene oxide is defi-.

nitely less reactive than propylene oxide. On the other hand, glycide may react with almost explosive violence and must be handled with extreme care.

The oxyalkylation of resins of the kind from which the initial reactants used in the practice of the present invention are prepared is advantageously catalyzed by the presence of an' alkali. Useful alkaline catalysts include soaps, sodium acetate, sodium hydroxide, sodium methylate, caustic potash, etc. The amount of alkaline catalyst usually is between 0.2% to 2%. The temperature employed may vary from room temperature to as high as 290 C. The reaction may be conducted with or without pressure, i. e., from zero pressure to approximately 200 or even 300 pounds gauge pressure (pounds per square inch). In a general way, the method employed is substantially the same procedure as used for oxyalkylation of other organic materials having reactive phenolic groups.

It may be necessary to allow for the acidity of a resin in determining the amount of alkaline catalyst to be added in oxyalkylation. For instance, if a nonvolatile strong acid such as sulfuric acid is used to catalyze the resinification reaction, presumably after being converted. into 16 a sulfonic acid, it may be necessary and is usually advantageous to add an amount of alkali equal ,stoichiometrically to such acidity, and include added alkali over and above this amount as the alkaline catalyst.

It is advantageous to conduct the oxyethylation in presence of an insert solvent such as xylene, cymene, decalin, ethylene glycol diethylether, diethyleneglycol diethylether, or the like, although with many resins, the oxyalkylation proceeds satisfactorily without a solvent. Since xylene is cheap and may be permitted to be present in the final product used as a demulsi her, it is our preference to use xylene. This is particularlytrue in the manufacture of products from low-stage resins, i. e., of 3 and up to and including 7 units per molecule. 7

If a xylene solution is used in an autoclave as hereinafter indicated, the pressure readings of course represent total pressure, that is, the combined pressure due to xylene and also due to ethylene oxide or whatever other oxyalkylating agent is used. Under such circumstances it may be necessary at times to use substantial pressures to obtain effective results, for instance, pressures up to 300 pounds along with correspondingly high temperatures, if required.

However, even in the instance of high-melting resins, a solvent such as xylene can be eliminated in either one of two ways: After the introduction of approximately 2 or 3 moles of ethylene oxide, for example, per phenolic nucleus, there is a definite drop in the hardness and melting point of the resin. At this stage, if xylene or a similar solvent has been added, it can be eliminated by distillation (vacuum distillation if desired) and the subsequent intermediate, being comparatively soft and solvent-free, can be reacted further in the usual manner with ethylene oxide or some other suitable reactant.

Another procedure is to continue the reaction to completion with such solvent present and then eliminate the solvent by distillation in the customary manner.

Another suitable procedure is to use propylene oxide or butylene oxide as a solvent as well as a reactant in the earlier stages along with ethylene oxide, for instance, by dissolving the powdered resin in propylene oxide even though oxyalkylation is taking place to a greater or lesser degree. After a solution has been obtained which represents the criginal resin dissolved in propylene oxide or butylene oxide, or a'mixture which includes the oxyalkylated product, ethylene oxide is added to react with the liquid mass until hydrophile properties are obtained. Since ethylene oxide is more reactive than propylene oxide or'butylene oxide, the final product may contain some unreacted propylene oxide or butylene oxide which can be eliminated by volatilization or distillation in any suitable manner.

Attention is directed to the fact that the resins herein described must be fusible or soluble in an organic solvent. Fusible resins invariably are soluble in one or more organic solvents such as those mentioned elsewhere herein. It is to be emphasized, however, that the organic solvent employed to' indicate or assure that the resin meets this requirement need not be the one used in oxyalkylation. Indeed, solvents which are susceptible to oxyalkylation are included in this group of organic solvents. Examples of such solvents are alcohols and alcohol-others. However. where a resin is soluble in an organic solvent, there are usually available other organic solvents which-- are-not susceptible to oxyalkylation, useful for the oxyalkylatiow step, In" any event, the organic solvent soiuble resin can be finely powdered, for instance to IQOto 200 mesh, and a slurry or suspension prepared xylene or the like, and subjected to oxyalkylatiorr. The fact that the resin is soluble in anorganic sol-' vent or the fact'that' it isfusibl'e 'ni'ans that consists of" separate molecules; Phenol-aldehyde resins of the type herein specified possess reac tive hydroxyl groupsand are oxyalkylation susceptble.

Considerable of whatis said immediately her-e inafter is. concerned with ability to vary the hydrophile properties" of the; hydriiriyl'ated intermediate reactants from minimum hydrophile propertes to maximum hydrophile properties. Such properties in turn, of'course, are efiected subsequently by the acid enemy-ea for esterifi cation and the quantitativenatureof the esterifi cation itself, i. e., whether it istotal or partial, and also by the hydroxylated glyoxalidine'used to obtairrthe' finalproduct ior use-1m the process of the present invention. It'jmay" be wen; however, to pointout" what has been said elsewhere in regard to the lriyd roiry'lated intermediate reactants. See, for example, ou'rf c'o pe'nding' applications, Serial Nosl 83730 and 8,731, bothn ed' February 16, 1948, and" serial No. 42,133, filed August 2, 1948; and" Serial No. 42,134, filed August 2, 1948 (all four cases'now abandoned). The reason is that the reactions, depending on the acid and the Hydroxylated glyox'alidine selected, may vary the hydroph le hydrophobe balance in one direction or the other, and also invariably cause'stlie development of somepioperty which makes it inherently difierent from the reactants fromwh'ich the derivative is' obtained. V

Referring to the hydrophile hvdioxy' ated in-' termediat'es, even more remarkable and eoually difiicult to explain, meme versatility and the' utility of these compounds considered as chem} ical reactants as one goes froin'minim'um hydro phile property to ultimate maiiimum hydrophile property. For instance; minimu livdrophile property maybe describedrouglily'as the point where two ethyleneoxy' radicals: or k moderately in excess thereof are introduced per phenolic hydroxyl. Such m nimum hydropliile property or subsurface-activity or minimum surface-' activity means that the product shows at least emulsifying properties or" en-entered; in cold or even in warmdistilledvi' aten (15 to 40 C.) in concentrations of- 0.5% to 550%. These mate rials are generally" more soluble in cold water than warm water, and may even be" very in soluble in boiling water. Moderately high temperatures aid in reducing the" viscosity of' the solute under examination. Sometimes if one continues to shake a hot-solution, even though cloudy or containing-an insolublepl'iase, one finds that solution takes place to give a'homogen'eous phase as the mixture cools. Such self-dispersion tests are conductedin the absence of an insoluble solvent.

When thehydrophile hydrophobe balance is All that one need to do is to have a Xylene solution within the range of 50 to parts by weight of oxyalkylated derivatives and 50 to 10 parts by weight of xylene and mix such solution with one, two or three times its volume of distilled water and shake vigorously so as to obtain an emulsion which may be of the oil-in-water type or the Water-in-oil type (usually the former) but, in any event, is due to the hydrophile-hydrophobe balance of the oxyalkylated derivative. We prefer simply to use the xylene diluted derivatives, which are described elsewhere, for this test rather than evaporate the solvent and employ any more elaborate tests, if the solubility is not sufiicient to permit the simple sol test in water previously noted.

If the product is not readily water soluble it may be dissolved in ethyl or methyl alcohol, ethylene glycol diethylether, or diethylene glycol diethylether, with a little acetone added if required, making a rather concentrated solution, for instance 40% to 50%, and then adding enough of the concentrated alcoholic or equivalent solution to give the previously suggested 0.5% to 5.0 strength solution. If the product is self-dispersing (i. e., if the oxyalkylated product is a liquid or a liouid solution self-emulsifiable), such sol or dispersion is referred to as at least semistable in the sense that sols, emulsions, or dispersions prepared are relatively stable, if they remain at least for some period of time. for instance 30 minutes to two hours, before showing any marked separation. Such tests are conducted at room temperature (22 C.). Needless to say, a test can be made in presence of an insoluble solvent such as 5% to 15% of Xylene, as noted in previous examples. If such mixture, i. e., containing a water-insoluble solvent, is at least semi-stable, obviously the solvent-free product would be even more so. Surface-activity re resenting an advanced hydrophile-hydrophobe balance can also be determined by the use of conventional measurements hereinafter described. One outstanding characteristic property indicating surface-activity in a material is the ability to form a permanent foam i dilute aqueous solution. for examp e. less than 0.5%, when in the higher oxyalkylated stage, and to form an emulsion in the lower and intermediate stages of oxyalkylation.

Allowance must be made for the presence of a solvent in the final product in relation to the hydrophile properties of the final product. The principle involved in the manufacture of the herein contemplated compounds for use as polyhydric reactants, is based on the conversion of a hydrophobe or nonhydrophile compound or mixture of compounds into products which are distinctly hydrophile, at least to the extent that they have emulsifying properties or are selfemulsifying; that is, when shaken with water they produce stable or semi-stable suspensions, or, in the presence of a water-insoluble solvent, such as xylene, an emulsion. In demulsification, it is sometimes preferable to use a product having markedly enhanced hydrophile properties over and above the initial stage of self-emulsifiability, although we have found that with products of the type used herein, most efiicacious results are obtained with products which do not have hydronhile properties beyond the stage of self-dispersibility.

More highly oxyalkylated resins give colloidal solutions or sols which show typical properties comparable toordinary surface-active agents.

Such conventional surface-activity may be meas-' ured by determining the surface tension and the interfacial tension against paraffin oil or the like. At the initial and lower stages of oxyalkyiation, surface-activity is not suitably determined in this same manner but one may employ a emulsification test. Emulsions come into existence as a rule through the presence of a surface-active emulsifying agent. Some surface-active emulsifying agents such as mahogany soap may produce a water-in-oil emulsion or an oil-in-water emulsion depending upon the ratio of the two phases, degree of agitation, concentration of emulsifying agent, etc. 7

The same is true in regard to the oxyalkylated resins herein specified, particularly in the lower stage of oxyalkylation, the so-called sub-surfaceactive stage. The surface-active propertiesvare readily demonstrated by producing a xylene-water emulsion. A. suitable procedure is as follows: The oxyalkylated resin is dissolved in an equal weight of xylene. Such 50-50 solution is then mixed with 1-3 volumes of water and shaken to produce an emulsion. The amount of xylene is invariably suflicient to reduce even a tacky resinous product to a solution which is readily dispersible. The emulsions so produced are usually xylene-in-water emulsions (oil-in-wa-ter type) particularly when the amount of distilled water used is at least slightly in excess of the volume of xylenesolution and also if shaken vigorously. At times, particularly in the lowest stage of oxyalkylation, one may obtain a water-in-xyleneemulsion (waterin-oil type) which is apt to reverse on more vigorous shaking and further dilution with water.

If in doubt as to this property, comparison with a resin obtained from para-tertiary butylphenol and formaldehyde (ratio 1 part phenol to 1.1 formaldehyde) using an acid catalyst and then followed by oxyalkylation using 2 moles of ethylene oxide for each phenolic hydroxyl, is helpful. Such resin prior to oxyalkylation has a molecular weight indicating about 4% units per resin molecule. Such resin, when diluted with an equal weight of xylene, will serve to illustrate the above emulsification test.

In a few instances, the resin may not be sufifi ciently soluble in xylene alone but may require the addition of some ethylene glycol diethylether as described elsewhere. It is understood that such mixture, or any other similar mixture, is considered the equivalent of xylene for the purpose of this test. p

In many cases, there is no doubt as to the presence or absence of hydrophile or surface-active characteristics in the polyhydric reactants used in accordance with this invention. They dissolve or disperse in water; and such dispersions foam readily. With borderline cases, i. e., those which show only incipient hydrophile or surface-active property (sub-surface-activity) tests for emulsifying properties or self-dispersibility are useful. The fact that a reagent is capable of producing a dispersion in water is proof that it is distinctly hydrophile. In doubtful cases, comparison can be made with the butylphenol-formaldehyde resin analog wherein 2 moles of ethylene oxide have been introduced for each phenolic nucleus.

The presence of xylene or an equivalent waterinsoluble solvent may mask the point at which a solvent-free product on mere dilution in a test tube exhibits self-emulsification. For this reason, if it is desirable to determine the approximate point where self-emulsification begins, then it is better to eliminate the xylene. or equivalent from a small portion of the reaction mixture and test such portion. In'some cases, such xylene-free resultant may show initial or incipient hydrophile properties, whereas in presence of xylene such properties would not be noted. In other cases, the first objective indication of hydrophile properties may be the capacity of the material to emulsifyan insoluble solvent such as xylene. It is to be emphasized that hydrophile properties herein referred to are such as those exhibited by incipient self-emulsification or the presence of emulsifying properties and go through the range of homogeneous dispersibility or admixture with water even in presence of added water-insoluble solvent and minor proportions of common elec-' trolytes as occur in oil field brines. V

Elsewhere, it is pointed out that an emulsification test may be used to determine ranges of surface-activity and that such emulsification tests employ a xylene solution. Stated another way, it is really immaterial whether a xylene solution produces a $01 or whether it merely produces an emulsion.

In light of what has been said previously in regard to the variation of range of hydrophile properties, and also in light of what has been said as to the-variation in theefiectiveness of various alkylene oxides, and most particularly of all ethylene oxide, to' introduce hydrophile character, it-

becomes obvious that there is a wide variation in the amount'of alkylene oxide employed, as long as it is at least 2 moles per phenolic nucleus, for producing products useful for the practice of this invention. Another variation is the molecular size of the resin chain'resulting from reaction between the difunctional phenol and the aldehyde such as formaldehyde.

tained varies somewhat with the conditions of reaction, the proportions of reactants, the nature of the catalyst, etc.

Based on molecular weight determinations, most of the resins prepared as herein described, particularly in the absence of asecondar heating step, contain 3 to 6 or '7 phenolic nuclei with approximately 4 /2 or 5 /2 nuclei as an average. More drastic conditions. of resinification yield resins of greater chain length. Such more intensive resinification is a conventional procedure and may .be employed if. desired. Molecular weight, of course, is measured by any suitable procedure, particularly by cryoscopic methods; but using the same reactants and using more drastic conditions of resinification one usually finds that higher molecular weights are indicated by higher melting points of the resins and a tendency to decreased solubility. See what has been said elsewhere herein in regard to a secondary step involving the heating of a resin with or without the use of vacuum.

Vie have previously pointed out that either an alkaline or acid catalyst is advantageously used in preparing the resin. A combination of catalysts is sometimes used in two stages; for instance, an alkaline catalyst is sometimes employed in a first stage, followed by neutralization and addition of a small amount of acid catalyst in a second stage. It is genzraliy believed that even in the presence of an alkaline catalyst, the number of moles of aldehyde, such as formaldehyde, mus-tbe greater than the moles of phenol employed in order to introduce methylol groups in the intermediate stage. There is no indication that such groups appear in the final resin if prepared by the use of an acid catalyst. It

It is well known that'the size and nature or structure of the resin polymer ob-' antigens is possible that such groups may appear in the finished resins prepared solely with an alkaline catalyst; but we "have never been able to confirm this ,iact in an examination oja large 1111. 11- ber of resins prepared ,by ourselves. Our preference, "howevenis to use an acid-catalyzed resin, particularly employing a formaldehyde-to.- phenol ratio of-I95 to 1.20 and, asfaras we'have been able 'to determine, such resins are freejrom methylolggroups. As a matter of fact, 'it'is probable that "in acid-catalyzed resinifications, the methylol structure may appear only momentarily at the verybeginn'ingof the reaction .and in all probability'is converted at oncej injto amore complex structure during "the intermediate stage.

One procedure which canbe employed in the use of a new resin to prepare pOlyhydric ,re-

'ac'tants 'for use in the preparation of compounds employed in the present invention, is to determine the hydroxyl value by the Verley-Bdls'ing method or its equivalent. Theresin as such, or in the form of ,a solution as described, is then treated with ethylene oxide in presence of 0.5% to of sodium methylate as a catalystinstepwisefashion. The conditions of reaction, ,asjar as time or per cent are concerned, are within the range previously indicated. With suitable agitation the ethylene oxide, if addedin molecular proportion, combines within a comparatively short time, for instance ,a jfew minutes to 2 .to Shoursgbutin some instances requires asnmuch as 13 to 24 hours. A useful temperature range isfrom 125 'to 225 The ,completion of the reaction of each addition of ethylene ,oxide .in Step-wise fashion is usually indicated by the, reducti'on or elimination of pressure. ,An amount conveniently used "for each addition ,is generally equivalent to a mole or .two moles of ethylene oxide per hydroxyl radical. "When :the ,amount of ethylene oxide added is equivalent to approximately "501% by weight of the original resin, :a sample is tested 'for'incipient,hydrophile propertiesby simply shaking up in water asis, or after theelimination of the solventli'f va solvent is present. The amount of ethylene oxide used ,toobtaina useful demulsifying agent .asa rule varies from "7.0% by weight of the original resin to as much as five or six times the weight of the original resin. In the case of a resin derived from para-tertiary'bufi lphenol, as little-as 50% by weight of ethylene oxide may give suitable solubility. *With propylene pxi'de, evena greater molecular proportion is requiredand sometimes a resultant of ,only limited hydrophile properties isobtainable. The sameis true to evenagreater extent with bu'tylene oxide. lfhe ,hydroxylated alkylene oxides are more effective, insolubilizing p per i than the c mparable compounds .in Which-no hydroxyl ispresent.

Attention is (directed to the fact that in the subsequent examples reference is made ,to the stepwise :addition of the ,alkylene oxide,,such.as ethyleneoxide. It is understood, 0f.co urse, ,there is no objection to the continuous .addition of alkylene oxide until .the desired stage ..of..reac.tion is reached. In fact, there :may ,be 'iless of .a hazard involved and .it is .o'ftengadvantageous to addzthealkylene oxide slowly in .a continuous stream and in such amount. as to, avoid exceeding the hi her pressures noted .in ,the various Texamplesor elsewhere.

It may be well .to emphasize the fact that when .resins are produced .from difunctional phenols and some of .-.the ,higher. aliphatic aldehrdes. such-ms acetaldehvde. the resultant is 2a eomparativelv sort or nitehelikeresinatprdine temperatures.- Such esins become .eomp a: .tively fluid at 1.10 to 165 .as .a rule, a d this can b readily .exyal ylated, pre a l m thyla e withouttheuseoi asolvent.

What has been .said prev ously i t t de t s g es that any experimen a i ary to determine ,the degree of oxyalkylation, and par icularly .oxy thvla ien W t h been sa d previously is submitted primarily to emphasize the fact that these remarkable oxyalkylated resins "having surface activity show unusual properties as the hydrophile character varies from a minimum 'to an ultimate maximum. One should not underestimate the utility of any of these polyhydric alcohols in a surfaoe active or subsurface-active range without examining them 7 by reaction with ,a number of the typical acids and hydroxyla'ted glyoxalidines herein described and subsequently examining the resultant for utility, either in demulsifi cation or in some other art or industry as referred to elsewhere, orasa reactant for the manufacture of more complicated derivatives. A few simple laboratory tests which ean be conducted in a routine manner will usually give all the information thatis required.

For instance, a simple rule to follow is to prepare a resinghaving at least three phenolicnuclei and being organic solvent-soluble. 'Qxyethylate such resin, using the following four ratios of moles of ethylene oxide per phenolic unit equivalent: 2 to 1; 6 to 1; 10 to 1; and 15 to 1. From a sample of each product -remove any solvent that may be present, such ,as xylene. Prepare 0.5% and 5.0% solutions in distilled water, as previously indicated. A mere examination of such series will generally reveal an approximate range of minimum hydrophile character moderate hydrophile character, and naximum hydrophile character. If the 2 to 1 ratio does not show minimum hydrophile character by test of the solvent-"free :product, then ;.Qne :should test its capacity toforman emulsion when admixed with xylene or otherinsolublezsol'vent. If neither test shows the required minimum hydrophile property, repetition'using 2. /2 120 4 moles per phenolic nucleus will serve. Moderate hydrophile character should i'bershownbyeither the 6 to 1 or 10 to 1 ratio. Such -;m oderate hydrophile character is indicated iby the :fact that :the sol in distilled water within the previously mentioned concentration range is;a permanent translucent 01 when viewed in acomparativelyfihin layer, for instance the -;depth ;of ;a ,test "tube. Ultimate hydrophile character ;is :usually shown'at the 15 to 1 ratio test; inthat -adding'a small'amount of an insoluble solvent,;1for instance;5% of xylene, yields a-product-whichwill give,atleastztemporarily, a transparent ,or translucent 5-501 :of the kind just described. ;-TI he-formation of a permanent foam, when-a 0:5 to -;5.0 aqueoussolution is shaken, is. an excellent test for surface-activity. Previous reference has been made :to the fact that other oxyal'kylatingagents may-require the use of in-- creased amounts of ralkylena oxide. "However, 'if onmdoes-not ,even'care j-togo to the trouble of calculatingmolecularweights, one can simply arbit-rarily -prepare compounds 1 containing ethylene oxide eguivalenttto about 5.0% -to by weight, for example 65% byrweight. ofthe-resin to be oxyethylatedka second example using approximately 200% to-300% by weight,rand-a third example using-about500%:?t o 150%1by weight, to explore thetenseszfihydrophileehydrophobebalance.

A practical examination of the factor of oxyalkylation level can be made by a very simple test using a pilot plant autoclave having a capacity of about 10 to 15 gallons as hereinafter described, Such laboratory-prepared routine compounds can then be tested for solubility and, generally speaking, this is all that is required to give a suitable variety covering the hydrophile-.hydrophobe range. All these tests, as stated, are intended to be routine tests and nothing more. They are intended to teach a person, even though unskilled in oxyethylation or oxyalkylation, how to prepare in a perfectly arbitrary manner, a series of compounds illustrating the hydrophile-hydrophobe range. I

If one purchases a thermoplastic or fusible resin on the open market selected from a suitable number which are available, one might have to make certain determinations in order to make the quickest approach to the appropriate oxyalkylation range. For instance, one should .know (a) the molecular size, indicating the number. of phenolic units; (1)) the nature ofthe aldehy dic residue, which is usually CH2; and (c) the nature of the substituent, which is usually butyl, amyl, or phenyl. With such information one is in substantially the same position as if one had personally made the resin prior to oxyethylation.

For instance, the-molecular weight of the internal structural units of the resin of the follow- 1 ing over-simplified formula:

OH OH OH 3 H it R R n R (n=1 to 13, or even more) is given approximately by the formula: (Mol. wt. of phenol 2) plus mol. wt. of methylene or substituted methylene radical. The molecular weight of the resin would be 11. times the value for the internal limit plus the values for the terminal units. The left-hand terminal unit of the above structural formula, it will be seen, is identical with the recurring internal unit except that it has one extra hydrogen. The right-hand terminal unit lacks the methylene bridge element. Using one internal unit of a resin as the basic element, a resins molecular weight is given approximately by taking (n plus 2) times the weight of the internal element. Where the resin molecule has only 3 phenolic nuclei as in the structure shown, this calculation will be in error by several per cent; but as it grows larger, to contain 6, 9, or 12 phenolic nuclei, the formula comes to be more than satisfactory. Using such an approximateweight, one need only introduce, for example, two molal weights of ethylene oxide or slightly more, per phenolic nucleus, to produce a product of minimal hydrophile character. Further oxyalkyla tion gives enhanced hydrophile character. A1 though we have prepared and tested a large number of oxyethylated products of the type described herein, we have found no instance where the use of less than 2 moles of ethylene oxide per phenolic nucleus gave desirable products.

Examples 11) through 18b, and the tables which appear in columns 51 through 56 of our said Patent 2,499,370 illustrate oxyalkylation products from resins which are useful as intermediates for 24 producing the quaternary ammonium compounds used in accordance with thepresent application, such examples giving exact and complete details for carrying out the oxyalkylation procedure.

The resins, prior to oxyalkylation, vary from tacky, viscous liquids to hard, high-melting olids Their color varies from a light yellow through amber, to a deep red or even almost black. Inthe manufacture of resins, particularly hard res-, ins, as the reaction progresses the reaction mass frequently goes througha liquid state to a sub-' resinous or semi-resinous state, often characterized'by being tacky or sticky, to a final complete resin. As the resin is subjected to oxyalkylation these same physical changes tend to take place in reverse. If one starts with a solid resin, oxyalkylation tends to make it tacky or semi-resin ous and further oxyalkylation makes the tackines disappear and changes the product toa liquid. Thus, as the resin is oxyalkylated it decreases in viscosity, that is, becomes more liquid or changes from a solid to a liquid, particularly when it is converted to the water-dispersible or water-soluble s tag'e. The color or the oxyalkylated derivative is usually considerably lighter than the original productfrom which it is made, varying from a pale straw color to an amber or reddish amber. The viscosity usually varies from that of an oil, like castor oil, to that of a thick viscous sirup. Some products are waxy. The

presence of a solvent, such as 15% xylene or the like, thins the viscosity considerably and also reduces the color in dilution. No undue significanceneed be attached to the color for the reason that if the same compound is preparedv in glass and in iron, the latter usually has somewhat darker color. If the resins are prepared as customarily employed in varnish resin manufacture, i. e., a procedure that excludes the presence of oxygen during the resinification and subsequent cooling of the resin, then of course the initial resin is much lighter in color. We have employed some resins which initially are almost water-white and also yield a lighter colored final product.

; Actually, in considering the ratio of alkylene oxide to add, and we have previously pointed out that this can be pre-determined using laboratory tests, it is our actual preference from a practical standpoint to make tests on a small pilot plant scale. Our reason for so doing is that we make one run, and only one, and that we have a complete series which shows the progressive effect of introducing the oxyalkylating agent, for instance, Our preferred proce-.

the ethyleneoxy radicals. dure is as follows: We prepare a suitable resin, or for thatmatter, purchase it in the open market.

We employ'8 poundsof. resin and 4 pounds-of.

xylene and place the resin and xylene in a suitable autoclave with an open reflux condenser- We prefer to heat and stir until the solution is a 20% to 30% solution, and remove the water of solution or formation. We then shut oiT the reflux condenser and use the equipment as an autoclave only, and oxyethylate until a total of Pounds of Ethylene Percentages Oxide Added, per

8-pound Batch qxyethylation to 750% can usually be completed within 30 hours and frequently more quickly.

The samples taken are rather small, for instance, 2 to 4 ounces, so that no correction need be made in regard to the residual reaction mass. Each sample is divided in two. One-half the sample is placed in an evaporating dish on the steam bath overnight so as to eliminate the xylene. Then 1.5% solutions are prepared from both series of samples, 1. e., the series with xylene present and the series with xylene removed. Mere visual examination of any samples in solution may be sufiicient to indicate hydrophile character or surface activity, i. e., the product is soluble, forming a colloidal sol, or the aqueous solution foams or shows emulsifying property. All these properties are related through adsorption at the interface, for example, a gas-liquid interface or a liquideliquid interface. If desired, surface activity can be measured in any one of the usual ways using a DuNouy tensiometer or dropping pipette, or any other procedure for measuring interfacial tension. Such tests are conventional and require no further description. Any compound having sub-surface-activity', and all derived from the same resin and oxyalkylated toa. greater extent, 1. e., those having a greater proportion of alkylene oxide, are useful as polyhydric reactants for the practice of this invention.

Another reason why we prefer to use a pilot plant testofthe kind above described is that we can use the same procedure to evaluate tolerance towards a trifunctional phenol such as hydrox-ybenzene or metaeresol satisfactorily. Previous reference has been made to the fact that one can conduct a laboratory scale test which will indicate whether or not a resin, although soluble in solvent, will yield an insoluble rubbery product, i. e., a product which is neither hydrophile nor surface-active, upon oxyethylation, particularly extensive oxyethylation. It is also obvious that one may have a solvent-soluble resin derived from a mixture of phenols having present 1% or 2% of a trifunctional phenol which will result in an insoluble rubber at the ultimate stages of oxyethylation but not in the earlier stages. In other words, with resins from some such phenols, addition of v2 or 3 rnolesof the oxyalkylating agent per phenolic nucleus, particularly ethylene oxide, gives asurface-activereactant whichis perfectly satisfactory, while more extensive oxyethylation yields an insoluble rubber, that is, an unsuitable reactant. I t isfobvious that this present procedure of evaluating trifunctional phenol tolerance is more suitable than the previous procedure.

It may be well to call attention to one result which may be noted in a long drawn-out oxyalkylation, particularly oxyethylation, which would not appear in a normally conducted reaction. Reference has been made to cross-linking and its eifect on soliibility and also the fact that, if carried far enough, it causes incipient stringiness, then pronounced stringiness, usually followed by a semi-rubbery or rubbery stage. Incipient stringiness, or even pronounced stringiness, or even the tendency toward a rubbery stage, is not objectionable so long as the final product is still hydrophile and at least sub-suriaceeactive. Such material frequently is best mixed with a polar solvent, such as alcohol or the like, and preferably an alcoholic solution is used. The point which we, want to make here, however, isthis: stringiness or rubberization at this stage may possibly be the result of etherification. Obviously if a difunctional phenol and an alddehyde produce a non-crossdinked resin molecule and if such molecule is oxyalkylated so as to introduce a plurality of hydroxyl groups in each molecule,

then and in that event if subsequent etherification takes place, one is going to obtain crossli in he same neral way that one would obtain crosselinking in other resinification reactions. Ordinarily there is little or no tendency toward etherification during the oxyalkylation step. If it does take place at all, it is only to an insignificant and undetectable degree. However,

suppose that a certain weight of resin is treated with an equal weight of, or twice its weight of, ethylene oxide. This may be done in a comparatively short time, for instance, at or C. in 4 to 8 hours, or even less. On the other hand, if in an exploratory reaction, such as the kind previously described, the ethylene oxide were added extremely slowly in order to take stepwise samples, so that the reaction required 4 or 5 times as long to introduce an equal amount of ethylene oxide employing the same temperature, then ether-i-fication might cause stringiness or a suggestion of rubberiness. For this reason if in an exploratory experiment of the kind previously described there appears to be any stringiness or rubberiness, it may be well to repeat the experiment and reach the intermediate stage of oxyalkylation as rapidly as possible and then proceed slowly beyond this intermediate stage. The entire purpose of this modified procedure is to cut down the time of reaction so as to avoid etherificationi f it be caused by the extended time period.

It may be well to note one peculiar reaction sometimes noted in the course of oxyalkylation, particularly oxyethylation, of the thermoplastic resins herein described. This effect is noted in a case where a thermoplastic resin has been oxyalk-ylated, for instance, oxyet-hylated, until it gives a perfectly clear solution, even in the presence of some accompanying water-insoluble solvent such as 10% to 15% of xylene. Further oxyalkylation, particularly oxyethylation, may then yield a product which, instead of giving a clear solution as previously, gives a very milky solution suggestin thatsome marked change has taken place. One explanation of the above change is that the structural unit indicated in the folloviring way where 8 is a fairly large number, for instance, 10 to 20, decomposes and an oxyalkylated resin representing a lower degree of termination and. likewise, the solvent used in deoxyethylation and a less soluble one, is generated termining molecular weight may not be suitable and a cyclic polymer of ethylene oxide is proas a solvent during oxyalkylation. For solution duced, indicated thus: of the oxyalkylated compounds, or their derivaca to nth HtH This fact, o u presents no difficulty for the tives a great variety of solvents may be employed, reason that oxyalkylation can be conducted in such as alcohols, ether alcohols, cresols, phenols, each instance stepwise, or at a gradual rate, and ketones, esters, etc., alone or with the addition samples taken at short intervals so as to arrive of water. Some of these are mentioned hereat a point where optimum surface activity or hyafter. We prefer the use of benzene or diphenyldrophile character is obtained if desired; for amine as a solvent in makingcryoscopic measproducts for use as polyhydric reactants in the urements. The most satisfactory resins are those practice of this invention, this is not necessary which are soluble in Xylene or the like, rather and, in fact, may be undesirable, i. e., reduce the *than those which are soluble only in some other solvent containing elements other than carbon and hydrogen, for instance, oxygen or chlorine.

efficiency of the product.

We do not know to what extent oxyalkylation produces uniform distribution in regard to phe- Such solvents are usually polar, semi-polar, or nolic hydroxyls present in the resin molecule. slightly polar in nature compared with xylene, In some instances, of course, such distribution cymene, etc.

can not be uniform for the reason that we have Reference to cryoscopic measurement is connot specified that the molecules of ethylene cerned with the use of benzene or other suitable ox d for eXample, he added in multiples of 1Jhe compound as a solvent. Such method will showunits present in the resin molecule This may that conventional resins obtained, for example, be illustrated in the following manner: f para tertiary amyiphenoi and formaide Suppose the resin happens to have five phenolic nuclei. If a minimum of two moles of ethylene oxide per phenolic nucleus are added, this would mean an addition of 10 moles of ethylene oxide, but suppose that one added 11 moles of hyde in presence of an acid catalyst, will have a molecular weight indicating 3,4,5 or somewhat greater number of structural units per molecule. If more drastic conditions of resiniethylene oxide, or 12, or 13, or 14 moles; obviousm are employed or if IQW'Stage resin 1y, even assuming the most uniform distribution 40 1s sub ected to a vacuum distillation treatment possible, some of the polyethyleneoxy radicals as previously described one Obtains a resin of would contain 3 ethyleneoxy units and some adistinctly higher molecular weight. Any molecwould contain 2. Therefore, it is impossible to u e weight determination us d. wh th r cryospecify uniform distribution in regard to the enscopic measurement 01' otherwise, other than the trance of the ethylene oxide or other oxyalkylat- ,45 conventional cryoscopic one employing benzene, ing agent. For that matter, if one were to inshould be checked so as to insure that it gives troduce 25 moles of ethylene 0X de re s 0 consistent values on such conventional resins as way to be certain that all chains of ethyleneoxy c trol, Frequently all that is necessary to units would have 5 units; there might be some having, for example, 4 and 6 units, or for that matter 3 or 7 units. Nor is there any basis for assuming that the number of molecules of the oxyalkylating agent added to each of the moleunake an approximation of the molecular weight range is to make a comparison with the dimer obtained by chemical combination of two moles of the same phenol, and one mole of the same cuies of the resin is the same, or different. Thus, I a.1dehyde under conditions to insure dimeriza' where formulae are given to illustrate or depict to the preparatmn of Such dlmers from the oxyaikyiated products, distributions of subst1tuted phenols, see Carswell, Phenoplasts,

cals indicated are to be statistically taken. We g The increased Viscosity resinous Charh however, included pecific, directions and actor, and decreased solubility, etc., of the highspecifications in regard to the totaljamount of polymers in Comparison With the dimer,

ethylene oxide, or total amount of any other que are a is equ red to establish that oxyalkylating agent, to add. the resin contains 3 or more structural units per In regard to solubility of the resins and the molecule.

oxyalkylated compounds, and for that matter Ordinarily, the oxyalkylationis carried out in derivatives of the latter, the following should be autoclaves provided with agitators or stirring noted. In oxyalkylation, any solvent employed devices. We have found that the speed of the should be non-reactive to the alkylene oxide emagitation markedly influences the reaction time. ployed. This limitation does not apply to sol- In some cases, the change from slow speed agivents used in cryoscopic determinations for obtation, for example, in a laboratory autoclave vious reasons. Attention is directedtothe fact agitation with a stirrer operating at a speed of that various organic solvents may be employed 60 to 200 R. P. M., to high speed agitation, with to verify that the resin is organic solvent-soluble. the stirrer operating at 250 to 350 R. P. M., re- Such solubility test merely characterizes the duces the time required for oxyalkylation by resin. The particular solvent used in such test about one-half to two-thirds. Frequently xylenemay not be suitable for a molecular weight desoluble products which give insoluble products by procedures employing comparatively slow speedkylene oxideis continuously fed to the ieactio'n vessel, with high speed agitation, i. e., an agitator operating at 250 to 350 R. P. M. Continuous cxyalkylation, other conditions being the same,- is more rapid than batch oxyalkylation, but the latter is ordinarily more convenient for laboratory operation.

Previous reference has been made to the fact that in preparing compounds of the kind herein described, particularly adapted for demulsification of water-in-oil emulsions, and for that matter for other purposes, one should make a complete exploration of the wide variation in hydrophobe-hydrophile balance as previously referred to. It has been stated, furthermore, that this hydrophobe-hydrophile balance of the oxyalkylated resins is imparted, as far as the range of variation goes, to a greater or lesser extent to the herein de cribed derivatives. This means that one employing the present invention should take the choice of the most suitable derivative selected from a number of representative compounds, thus, not only should a variety of resins be prepared exhibiting a variety of oxyalkylations, particularly oxyethylations, but also a variety of derivatives. This can be done conveniently in light of what has been said previously. From a practical standpoint, using pilot plant equipment, for instance, an autoclave having a capacity of approximately three to five gallons. We have made a single run by appropriate selections in which the molal ratio of resin equivalent to ethylene oxide is 1 to 1, 1 to 5, 1 to 10, 1 to 15, and l to 20. Furthermore, in making these particular runs we have used continuous addition of ethylene oxide. In the continuous addition of ethylene oxide We have employed either a cylinder of ethylene oxide without added nitrogen, provided that the pressure of the ethylene oxide was sufficiently great to pass into the autoclave, or else we have used an arrangement which, in essence, was the equivalent of an ethylene oxide cylinder with a means for injecting nitrogen so as to force out the ethylene oxide in the manner of an ordinary seltz er bottle, combined with the means for either weighing the cylinder or measuring ;the ethylene oxide used volumetrically. Such procedure and arrangement for injecting liquids is, of course, conventional. The following data sheets exemplify such operations, i. e., the combination of both continuous agitation and taking samples so as to give five different variants in oxyethylation. In adding ethylene oxide continuously, there is one precaution which must be taken at all times.

7 The addition of ethylene oxide must stop immediately if there is any indication that reaction is stopped or, obviously, if reaction is not started at the beginning of the reaction period. Since the addition of ethylene oxide invariably an exothermic reaction, whether or not reaction has taken place can be judged in the usual manner by observing (at) temperature rise or drop, if any, (b) amount of cooling water or other means requir'ed to dissipate heat of reaction; thus, if there is a temperature drop without the use of cooling water or equivalent, or if there is no rise in temperature without using cooling water control, careful investigation should be made.

In the tables immediately following, we are showing the maximum temperature which is usually the operating temperature. In other words, by experience we have found that if the initial reactants are raised to the indicated temperature and then if ethylene oxide is added slowly, this temperature is maintained by cooling water until the oxyethylation is complete. We have also indicated the maximum pressure that we obtained or the pressure range. Likewise, we have indicated the time required to inject the ethylene oxide" as well as a brief note as to the solubility of the product at the end of the oxyethylation period. As one period ends it will be noted we have removed part of the oxyethylated mass to give us derivatives, as therein described; the rest has been subjected to further treatment. All this is apparent by examining the columns headed Starting mix, Mix at end of reaction, Mix which is removed for sample, and Mix which remains as next starter.

The resins employed are prepared in the manner described in Examples 1a through 103a of our said Patent 2,499,370, except that instead of being prepared on a laboratory scale they were prepared in 10 to 15-gallon electro-vapor heated synthetic resin pilot plant reactors, as manufactured by the Blaw-Knox Company, Pittsburgh, Pennsylvania, and completely described in their Bulletin No. 2087 issued in 1947, with specific reference to Specification No. 71-3965.

For convenience, the following tables give the numbers of the examples of our said Patent 2,499,370 in which the preparation of identical resins on laboratory scale are described. It is understood that in the following examples, the change is one with respect to the size of the operation.

The solvent used in each instance was xylene. This solvent is particularly satisfactory for the reason that it can be removed readily by distillation or vacuum distillation. In these continuous experiments the speed of the stirrer'in the autoclave was 250 R. P. M.

In examining the subsequent tables it will be noted that if a comparatively small sample is taken at each stage, for instance, ,4; to one gallon, one can proceed through the entire molal stage of 1 to 1, to 1 to 20, without remaking at any intermediate stage. This is illustrated by E):- ample 1041). In other examples we found it desirable to take a larger sample, for instance, a 3-gallon sample, at an intermediate stage. As a result it was necessary in such instances to start with a new resin sample in order to prepare sufficient oxyethylated derivatives illustrating the latter stages. Under such circumstances, of course, the earlier stages which had been previously prepared were by-passed or ignored. This is illustrated in the tables where, obviously, it shows that the starting mix was not removed from a previous sample.

Date, J une 22, 1948 A tdehyde for resin: F

ormaldehyde [Resin made in pilot plant size batch, approximately 25 pounds, corresponding to 3a of Patent 2,499,370 but this batch designated 104a] Date, June 18, 1948 Phenol for resin: Nonylphenol Aldehyde for resin: Formaldehyde QS Quite soluble.

Mix Which is Mix Which Re- Starting Mix fig ggg of Removed for mains as Next Sample Starter Max. Max

Pressure Tempera- Tim Solubility lbs sq in ture Lbs. lfibs. Lbs abs. Lbs fibs. Lbs Ibs. Lbs Soleso es- 0 es- 0 esvent in Eto vent in Eto vent in Eto vent in Eto First Stage Resin to EtO Molal Ratio 1:1 14.25 15.75 0 14.25 15. 75 4.0 3.35 3.65 1.0 10.9 12.1 3.0 80 150 $4 I Ex.No;"104b Second Stage Resin to Et0. Molal Ratio 1:5 10.9 12.1 3.0 10. 9 l2. 1 15. 3. 77 4. 17 5.31 7. 13 7. 93 9.94 70 158 16 ST Ex. No. 105b.

Third Stage Resin to 12150.... Molal Ratio 1:10. 7.13 7.93 9. 94 7. 13 7. 93 19.69 3. 29 3.68 9. 04 3. 84 4. 25 10.65 60 173 $6 FS Ex.No.106b

Fourth Stage Resin to EtO. Molal Ratio 1:15- 3. 84 4. 25 10.65 3. 84 4. 25 16.15 2. 04 2.21 8. 1.80 2.04 7. 220 160 $6 RS Ex. No. 107b Fifth Stage Resin to EtO. Molal Ratio 1:20- 1.80 2.04 7.60 1.80 2.04 10.2 100 150 1?; Q8 Ex. N0.108b

I=Insoluble. ST==Slight tendency toward becoming soluble. FS=Fairly soluble. RS=Readi1y soluble.

[Resin made in pilot plant size batch, approximately 25 pounds, corresponding to a of Patent 2,499,370 but this batch designated 109a.]

, Mix Which Re- Mix Which is Starting Mix kxg ggg of Removed for mains as Next Sample Starter Max. Max. Time Pressure Temperahrs Solubility Lbs. Lbs. Lbs. Lbs. Lbs. Lbs. Lbs. Lbs. Sol- Res- Sol- Res- 23 301- Res- ,51% Sol- Res- 1 vent in vent in vent in vent in First Stage Resin t0 EtO M0131 Ratio 1:1 15. 0 15. 0 0 15. O 15. 0 3 5. 0 5. 0 1. 0 10.0 10. 0 2. 0 50 150 1% ST Ex. No. 109b Second Stage Resin t0 EtO- Molal Ratio 1: 10 10 2. 0 10 10 9. 4 2. 72 2. 72 2. 56 7. 27 7. 27 6. 86 147 2 D'I Ex. N0. 1101)..."

Third Stage Resin to EtO Molal Ratio 1:10. 7. 27 7. 27 6. 86 7. 27 7. 27 13. 7 4. 16 4. 16 7. 68 3. 15 3. 15 5. 95 1% S Ex. No. 111b Fourth Stage H Resin to EtO Molal Ratio 1:15. 3.15 3.15 5.95 3. 15 3. 15 8.95 1.05 1.05 2.95 2. 10 2. 10 6.00 220 174 2% S Ex. N0.112b

Fifth Stage fi i l r? 1 1 26' 2 0 o 0 a a i0 10 2. 10 6. 00 2. 1 2. 1 8. 00 220 S Ex. No. 113b 18? as v S Soluble. ST Slight tendency toward solubility.

VS =Very soluble.

Date, June 23, 14, 1948 tile sin made ii: pilot a fioand's f'cor respoadin 1 Aldehyde for resin: Formaldehyde g to So of Patent 2,499,370 but this batch designated 114a] Mix whicii is MixWhich Re- Starting Mix I gg ggg Removed for mains as Next Sample arter I Max. Max. Time I lErasure 'femp eroahrs Y Solubility Lbs. Lbs. Lbs. 'Lbs. iLbs. Lbs. Lbs. Lbs.

Lbs. Lbs. Lbs Lbe. Sol- Res- 801- Resf 801- Res- Soi- Res- M vex t in vent in vent in Eto vent in Eto Firet Stage Resin to Et0 3 1 Molal Ratio 111-. 14.2 15.8 0 14.2 15.8 3.25 3.1 3.4 0.75 11.1 12.4 2.5 150 1%: NS Ex. N0. 1141)"... 5

Second Stage Resiu'to EtO 1. Molal Ratio 1 11.1 12.4 2.5 11.1' 12.4" 12.5 7.0 7.82 7.88 4.1 4.58 4. 62 171 34 SS Ex. No. nab--- Third Stage Resin to EtO..." 1 M01211 Ratio 1:10. 5.64 7. 36TH 6.04 7.36 15.0 190 1% S Ex. No. 116b Fourth Stage Resiato mom- 5 g F M0151 Ratio 1:15- 4.40 4.9 '0 4. 4'' 419 14.? 400 160 M VS Ex. No. 1m--- Fifth Stage Resin to Et0. M01211 Ratio 1:20 41 4. 58 4. 62 4. 1" 4. 58 '18. 52 260 172 H; VS Ex. N0. 118b- S=So1uble. NS=-Not soluble. ss --So1i1'ebrhat"so1uble. VS=Very soluble.

Date, July 8'13, 1948 [Resin made in pilot plant size batch Aldehyde for reein: Formaldehyde corresponding to 69a of Patent 2,499,370 but this batch designated 119a.]

Starting :Mix':

1.... at Em a 5 Reaction...

, approximately 25 pounds,

' Mix Which is Removed for Sample Starter Mix Which Remains as Next m wmio.

L bs. Resm a Lbs- .EtO-

Lbs. Solvent- Lbs. Resin Pressure lbs. sq. in.

Max.

Tempera- Max.

tare, C.

Time,

Solubility First Stage Molai Ratio 1 Ex. No. 1190..----

Second Stage Resin to E'tOt... MkflaY'Rsitio 1:5. Ex. N0. 12Gb Third Stage Resin teams..- Molal Ratio ;1:10 Ex. No. 12111,... I

Fourth Stage Fifth Stays 1 Moial Ratio S==Solub1e.

NS Not soluble.

VS=Very soluble.

Phenol for iesz'n: Para-secondary butylphenol I Aldehydefor re sin: E'zirbhaldehyde Date, Jul 14-15, 1948 m i P l 212 115222121 1 1 95 215. 12 99 .14%.2922 999915229 +1 9 2 1E? M1 11,111.51. 15.51.1051..- Starting M x gg figg Rembyed I61 mains.zis..leit g; I II Starter -Mdx- I ,l,ll;rgssure ,f tlfle nngga fflime Solubility l I i I s.sq. in. are rs. 52?: 532: 3 521 231; 1 11?; 1 vent in vent in I I i I II I II I First Stabs I Resin to EtO I I; II I II I I Molal Ratio 1: 1 14.45 15. 55 0 14. 15. 4. 25 5. 97 6. 38 1. 8. 48 9. 17 2. 50 60 150 51: NS Ex. No. 1240 j v Second Stizge I Resin to Em--. V I I Mo]al, Rati0 1=5- 8 45 9.17 2.50 8. 45 9.17 16.0 5.83 6. 32 11.05 2. 55 2.85 4.95 95 188 )5 BS Ex. No. 125b 1 Third Stage Resin to Et( Molal. Ratio 1:10. 4. 82 5.13 0 4.82 5.18 14.25 400 83 $5 8 Ex. N0. 12Gb I Fourth Stizge Resin to EtC Molal Ratio 1 5- a 85 4.15 0 3.85 4.15 17.0 I 120 0 35 VS Ex. No. 12717 1 1 l Fifth smge Resin to EtO 5 3 Moial Ratio 1:20- 2.65 2.85 4.95 2.65 2.85 15.45 80 170 "91;: VS Ex. No. 128D I I Phenol for resin: Menthyl Aldehyde for resin: Propionaldehyde Date August 12-13, 1948 [Resin made on pilot plant size batch, approximately 25 pounds, corresponding to 81a of Patent Mix Which is Mix ivmch Re- Starting Mix g figg of Remmzed for mains as Next j Sample Starter wMax. Time I I I I Pr essure Tem gera- .l Solubility .lblsii Ifibs; gibs. r 1 abs. 23 S l kbs. mm

o eso es- 0- es- 4 0 es vent m 1 2, F jYl F First Stake 1 Resin t0 E tO 1 1 Mola] Rat1o1:1- 12. 8 17. 2 12. 8 17. 2 2. '75 4.25 5. 7 0. 95 8.55 11.50 I30 110 150 $6 Not soluble. EX. N0. 12% I v Second Sthge Resin to Etc)..." 1 r l I 140121 Rati0'1:5 8 55 11. 50 1. 80 8. 55 11. 50 9. 3 4. 78 6.42 5. 2 3. 77 5.08 4.10 170 P6 Somewhat Ex. No. 1300 I jI 'sblu'b'le.

Third sm e f Resin to EtO I 'g n 1401a! Ratio 1:10- 3 77 5. 08 4. 10 3. 77 5. 0B 13. 1 100 182 M2 Soluble. 3x. No. 1315 I II I 1 Fourth Stizge 388111 E50--- I l i I 5 401a] Ratlo 1:15- 5 2 7.0 5.2 7.0 17.0 3.10 4. 17 10.13 2.10 2.83 6.87 200 182 54 Verysoluble. Ex. N o. 1321)--.. J

Fifth Stake 85111120 E"--. I I I 101211 R5313?) 1:20 2 10 2.83 6. 87 2. 1O 2. 83 9. 12 90 $6 Verysoluble.

Phenol. forresz'n: Para-tertiary amylphenol Date, August 27-31, 1948 Aldehyde for resin: Furfural [Resin made on pilot plant size batch, approximately 25 pounds, corresponding to'42a oi Patent2,499,370 but this batch designated as134m] Mix Which is Mix Which Re- Starting Mix figg figg or Removed formains as Next Sample Starter Max. Max. Time Pressure Temp era- Solubility i b s. abs. Lbs I b s. m. Lbs 1 13 5. I bs. Lbs lbls. I bs. Tbs

oeses- .oes- V 0- es vent in Eto vent in Eto ventin Eto vent in Eto First Stage Resin to 1H0"..- MolalR:1tio1:1 11.2 18.0 11.2 18.0 3.5 2.75 4.4 0.85 8.45 13.6 2.65 120 135 36 Not Soluble. Ex:No. 13 1b Second Stage Resin to Et0 MolalRatio1:5-. 8.45 13.6 2.65 8.45 13.6 12.65 5.03 8.12 7.55. 3.42 5.48 5.10 110. 150 $4 Somewhat Ex. No.135b i soluble.

Third Stage Resin to FtO Mola]Rati01:10-. 4.5 8.0 4.5 8.0 14.5 2.45 4.35 7.99. 2.05 3.65 6.60 180 163 $6 Soluble. Ex. No. 136b Fourth Stage Resin to EtO Molal Ratio 1:15-. 3.42 5. 48 5.10 3.42 5.48 15.10 180 188 M; Verysoluble. Ex. N0. 137!) Fifth Stage Resin to Et0-- Mola] Ratio 1:20.. 2.05 3.65 6.60 2.05 3.65 13.35 120. 125 M; Verysolubie. Ex. No. 13811 Phenol for resin: Menthyl Date, Sept. 23-24, 1948 [Resin made on pilot size batch, approximately 25 pounds, corresponding to 8911 ofPatent 2,499,370 but this batch designated as 13941.]

Aldehyde for resin: Furfural Mix Which is Mix Which Re- Starting Mix 223 of Removed for mains as Next c Sample Starter 1 Max. Max. Tim

Pressure Tempgrahrs Solubility I b s. I bs. Tbs r b s. gbs. Lbs Ibls. gbs. Lbs I b s. gbs. Lbs ture,

oesoes- 0- es- 0- esvent in Em vent in Eto vent in Eto vent in Eto First Stage Resin to EtO- Molal Ratio 1:1- 10.25 17. 10.25 17.75 2.5 2.65 4.60 0.65 7.6 13.15 1.85 150 56 Not soluble. Ex. No. 139!) Second Stage Resin to Et0 Molal Ratio 1: 7.6 13.15 1.85 7.6 13.15 9.35 5.2 9.00 6.40 2.4 4.15 2. 80 177 $6 Somewhat Ex. No. 14Gb soluble.

Third Stage Resin to EtO.- Molal Ratio 1:10 4. 22 6. 98 4. 22 6.98 10.0 90 165 ti Soluble. Ex. No. 14112- Fourth Stage Resin to EtO .VIolal Ratio 1:15-. 3. 76 6.2 3. 76 6.24 13.25 100 171 16 Very soluble. Ex. No. 14212 Fifth Stage Resin to EtO .VIolal Ratio 1:20 2. 4 4. l5 2. 95 2.4 4. 15 11. 70 90 34; Very soluble. Ex. No. 1436 2542,0719 v a 4o Phenol fonre'sin: Pam-octyl Aldehyde for resin. Furfural Date. October 7-8. 1948 [Resin made on pilot plant size batch. approximately 25 pounds. corresponding to 42a of Patent 2.499.370 with 206 parts by weight of commercial para-octylphenol replacing 164 parts by weight of para-tertiary amylphenol but this batch designated as 14411.]

I Mix Which is Mix Which Re- Starting Mix figg figg of Removed for mains as Next Sample Starter Max. Max. Tim Pressure Tempglahm Solubility Lbs. Lbs. Lbs Lbs. Lbs. Lbs Lbs. Lbs. Lbs Lbs. Lbs. Lbs Sol- Res- Sol- Res- Sol- Res- Sol- Resvent in vent in vent in vent in Fzrst Stage Resin to Et0 Y Molal Ratio 1:1.. 12 1 18.6 12.1 18.6 3.0 5. 38 8. 23 1.34 6.72 10.32 1.66 80 150 M2 Insoluble. Ex. No. 144b.-.-

Second Stage Slight tend- Resin to EtO.... ency to- Molal Ratio 1:5-- 9 25 14.25 9. 25 14.25 11.0 3.73 5.73 4.44 5. 52 8.52 6.56 100 177 942 ward be- Ex. No. 14512..... coining soluble.

Third Stage ResintoEtO.--. V Molal Ratio 1:10. 6 72 10.32 1.66 6.72 10. 32 14.91 4. 97 7.62 11.01 1.75 2.70 3.90 85 182 $4 Fairly solu- Ex. No. 146b.-. ble.

Fourth Stage Resin to Et0... Molal Ratio 1:15- 5 52 8. 52 6.56 5.52 8. 52 19.81 100 176 $6 Readily sol- Ex. No. 147b.... uble.

Fifth Stage Resin to EtO. Molal Ratio 1:20. 1. 75 2.70 3.90 1.75 2.70 8.4 80 160 $4 Quite solu- Ex. No. 148b.--.- ble.

Phenol for resin: Para-phenyl Aldehyde for resin: Furfural Date. October 11-13, 1948 [Resin made on pilot plant size batch. approximately pounds, corresponding to 4211 of Patent 2,499.370 with 170 parts by weight of commercial paraphenylphenol replacing 164 parts by weight of para-tertiary amylphenol but this batch designated as 14911.]

Mix Which is Mix Which Re- Starting Mix g gg ggg of Removed for mains as Next Sample 7 Starter Max Max I Pressure Tempsra- 2:2? Solubility r b sv abs. Lbs Ibls. gbs. Lbs gbls. abs. Lbs gbis. Ifibs. Lbs

o eso es- 0 eso esvent in Eto vent in Eto vent in Eto vent in Eto First Stage Resin to EtO Molal Ratio 1 l3. 9 16.7 13. 9 16. 7 3.0 3. 50 4. 25 0. 80 10.35 12. 45 2. 20 100 160 k; Insoluble. Ex. No. 1496-.-

Second Stage 7 Resin to EtO.. Slight end- Molal Ratio 1: 10. 12. 2. 20 10. 35 12.45 12. 20 5. 15 6.19 6.06 5. 20 6. 26 6. 14 183 )4; encdy Ex. N0. 1501;"..-

bllity.

Third Stage Resin to EtO. Molal Ratio 1:10- 8 10. 7 8.90 10.70 19.0 5.30 6.38 11. 32 3. 60 4. 32 7.68 90 193 A2 Fairly solu- Ex. No. 1511)- ble.

Fourth. Stage Resin to Et0 Molal Ratio 1:15. 5. 20 6.26 6.14 5.20 6. 26 16.64 171 $6 Readily Sol- Ex. No. 1525..." uble.

Fifth Stage Resin to EtO.-..

Molal Ratio 1:20. 3.60 4.32 7.68 3.60 4.32 15. 68 Sample somewhat rubbery and gelat- 230 2 -Ex. No. 153b..-.- Y Y Y inous but fairly soluble 

1. A PROCESS FOR BREAKING PETROLEUM EMULSIONS OF THE WATER-IN-OIL TYPE, CHARACTERIZED BY SUBJECTING THE EMULSION TO THE ACTION OF A DEMULSIFIER INCLUDING A HYDROPHILE QUATERNARY AMMONIUM COMPOUND OBTAINED BY REACTION BETWEEN A HYDROXYLATED GLYOXALIDINE OF THE FORMULA: 